We would use an inert electrode in the cell diagram when the oxidization or reduction side do not have a solid metal. In Fe^3(aq) + e- --> Fe^2+(aq), we would use Pt(s) or C(graphite) to act as the filler metal since the oxidation/reduction side don't have a metal.